Graphite is widely used as a material for Continuous casting molds. Continuous casting is a casting method in which the steps of pouring, solidification and withdrawal (extraction) of the casting from an open end mold are carried out continuously. Graphite molds (dies) may be used in both types of the process: vertical continuous casting and horizontal continuous casting . Most molds are fabricated from isostatically pressed graphite, however extruded graphite is also used for vertical casting of large ingots. The following alloys are manufactured by continuous casting in graphite molds:

• Low wettability

In order to prevent sticking and breaking a casting extracted from the mold its material should possess poor adhesion to the solidifying metal. It is achieved by low wetting of the mold by the liquid metal. Graphite is not wettable by most molten non-ferrous metals and alloys. Ferrous alloys (eg. Cast irons) wet graphite due to the reaction with carbon, which results in formation of carbides Fe3C. Graphite is also wetted by alloys containing nickel (more than 6% of nickel), zinc or tin.

• High thermal conductivity

Heat liberated during cooling down and solidification of the cast metal should be removed from the mold. The value of the heat transferred through the mold in a time unit determines the solidification rate and the pulling (extraction) speed of the casting. Thermal conductivity of the mold material should be high enough to provide fast heat removal. Thermal conductivity of graphite used for continuous casting molds is in the range 560-960 BTU*in/hr*ft²*ºF (80-140 W/m*K), which is comparable to thermal conductivity of metals: aluminum BTU*in/hr*ft²*ºF (222 W/m*K); steel 450 BTU*in/hr*ft²*ºF (65 W/m*K). Thermal conductivity of graphite depend on temperature: it decreases to a half as the temperature rises to °F (704°C).

• Low coefficient of thermal expansion

Casting mold is heated inside by the entering molten metal and cooled down from the outside by the water-cooled copper jacket (or directly by water). The resulting temperature distribution throughout the mold is extremely non-uniform. Low thermal expansion of the mold material helps to prevent distortion the mold shape and secures the casting geometry. Thermal expansion of graphite is 2-2.8*10-6 °F-1 (3.5-5*10-6 °C-1), which is considerably lower than that of metals: aluminum 13*10-6 °F-1 (23*10-6 °C-1); steel 7*10-6 °F-1 (13*10-6 °C-1).

• High thermal shock resistance

Thermal shock resistance of a material may be estimated in accordance to the formula:

Rs = (λ*σF)/(α*E)

If you want to learn more, please visit our website Zhongsheng.

Where: Rs' thermal shock resistance; λ- thermal conductivity; σF' flexural strength; α- coefficient of thermal expansion (CTE); E' modulus of elasticity.
Graphite has excellent thermal shock resistance due to favorable combination of high thermal conductivity, low coefficient of thermal expansion, low modulus of elasticity ( ksi / 10.3 GPa) and relatively high flexural strength ( psi / 52 MPa).

• Self-lubrication

Graphite is a solid lubricant. Low friction between the mold surface and the solidifying metal ensures smooth withdrawl (extraction) of the casting without cracks and minimizes thickness of the defective periferial skin. Specific layered crystal structure of graphite determines its self-lubricating properties providing low friction without additional oil lubrication.

• Good mechanical strength

In contrast to other materials mechanical strength (tensile strength, compressive strength, flexural strength) of graphite increases with a temperature rise.

• Good machinability

Graphite is easily machined. Molds of complicated shapes with close tolerances may be obtained by milling, turning, sawing, grinding and surface finishing. Fine finish of the inner mold surface (ground or polished) is important for decrease of the material wettability and friction. Good quality of the outer surface ensures minimal air gap between the mold and the water-cooled jacket, which results in better heat transfer.

to top

The Process

Initially, one of our custom mold specialists will discuss the project you are interested in having customized to review your desired specifications or design. You have the option to provide any artwork, logos, or specific dimensions. Following this, we will provide you with a price quotation, approximate lead time, and answer any questions that you may have in regards to your order. You will also be provided with a digital proof of your design to approve before it goes into final production.